| YUCLAIR PD800F is medium density polyethylene resin with broad molecular weight distribution and relatively low melt index of 0.25 g/10min. It offers a high degree of cold temperature impact resistance, stress crack resistance and toughness combined with good processability. Application / Use Case: Pipe&& |
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.25 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | > 1000 | hr | ASTM D1693 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 23.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 950 | % | ASTM D638 |
| Bending modulus | 706 | MPa | ASTM D747 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -80.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 121 | ℃ | ASTM D1525 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |