| About |
|---|
| YUNCON® M90 is an Acetal (POM) Copolymer product. It can be processed by extrusion or injection molding and is available in Asia Pacific, Europe, or North America. Applications of YUNCON® M90 include engineering/industrial parts and automotive. Characteristics include: Flame Rated Chemical Resistant Bacteria Resistant Copolymer Fatigue Resistant&& |
| Product Description | |
|---|---|
| Supplier | YunTianHua |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Low warping,Alkali resistant,Good Dimensional Stability,Good Electrical Properties,Good liquidity,Good Hardness,Antimicrobial properties,Low coefficient of friction,Acidproof,Fatigue resistance,Copolymer,Good wear resistance,Solvent resistance,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 9.0 | g/10min | ISO 1133 |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2600 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 61.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 35 | % | ISO 527-2 |
| Bending modulus | 2600 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179-1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 95.0 | ℃ | ISO 75-2/A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 160 to 180 | °C | |
| Barrel middle temperature | 170 to 200 | °C | |
| Barrel front temperature | 190 to 210 | °C | |
| Nozzle temperature | 180 to 210 | °C | |
| Processing (melt) temperature | 180 to 210 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Injection pressure | 50.0 to 100 | MPa | |
| Hold pressure | 30.0 to 80.0 | MPa | |
| Back pressure | 0.00 to 0.500 | MPa | |
| Screw speed | 50 to 120 | rpm | |
| Melt temperature | 180 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |