| About |
|---|
| YUNGSOX® PP 1040 is a Polypropylene Homopolymer (PP Homopolymer) material. It is available in Asia Pacific. Important attributes of YUNGSOX® PP 1040 are: Flame Rated Good Stiffness Heat Resistant Homopolymer Typical applications include: Appliances Consumer Goods Food Contact Applications Household Applications&& |
| Product Description | |
|---|---|
| Supplier | fpc-tw |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Homopolymer,Good Rigidity,Heat Resistance, Good,High Heat Resistance,HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 23±2℃，50±5% RH | 0.9 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 5.0 | g/10min | ISO 1133 |
| Shrinkage rate | 1.3 to 1.7 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.0 | KJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 115 | ℃ | ISO 75 |
| Vicat Softening Temp | 155 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 50 mm/min, 4mm | 34.3 | MPa | ISO 527-2 |
| Bending modulus | |||
| 2 mm/min，4mm | 1370 | MPa | ISO 178 |
| elongation at break | |||
| 50 mm/min,4mm | 550 | % | ISO 527 |
| Rockwell hardness | |||
| R scale | 105 | ISO 2039-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |