YUPLENE® BX3820

About
YUPLENE BX3820 is a high crystalline propylene impact copolymer designed for injection molding applications. YUPLENE BX3820 has excellent properties in stiffness, flow, mechanical properties, heat resistance and impact strength, which make YUPLENE BX3820 suitable for auto parts, electric appliances, large size containers, thin wall and very high speed injection applications. This is not a chemical cracked grade so it is free from surface gas mark. YUPLENE BX3820 can reduce various injection problems such as surface trouble, shrink, warpage etc. and reduce the cycle time of injection molding due to rapid crystallization.&&

About

YUPLENE BX3820 is a high crystalline propylene impact copolymer designed for injection molding applications. YUPLENE BX3820 has excellent properties in stiffness, flow, mechanical properties, heat resistance and impact strength, which make YUPLENE BX3820 suitable for auto parts, electric appliances, large size containers, thin wall and very high speed injection applications. This is not a chemical cracked grade so it is free from surface gas mark. YUPLENE BX3820 can reduce various injection problems such as surface trouble, shrink, warpage etc. and reduce the cycle time of injection molding due to rapid crystallization.&&

Product Description
Supplier	SKC
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Rigidity,High impact resistance,High liquidity,Crystal,High Heat Resistance,Impact copolymer
Availabilitys	North America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Melt Flow Rate
230℃，2.16kg	40	g/10min	ASTM D1238
Spiral flow length	> 80.0	cm	Internal Method

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ASTM D256
-20℃	34	J/m	ASTM D256
23℃	64	J/m	ASTM D256

Aging performance	Nominal value	Unit	Test method
Oven Aging	15.0	day	ASTM D3012

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	155	℃	ASTM D1525
Hot deformation temperature	135	℃	ASTM D648

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	102		ASTM D785
tensile strength
yield	32.4	MPa	ASTM D638
Tensile strain
fracture	< 200	%	ASTM D638
Bending modulus	1860	MPa	ASTM D790

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.