YUPLENE® BX3900

About
Y UPLENE BX3900 is a high crystalline propylene impact copolymer designed for injection molding applications. YUPLENE BX3900 has excellent properties in stiffness, flow, mechanical properties, heat resistance and impact strength, which make YUPLENE BX3900 suitable for auto parts, electric appliances, large size containers, thin wall and very high speed injection applications. This is not a chemical cracked grade so it is free from surface gas mark. YUPLENE BX3900 can reduce various injection problems such as surface trouble, shrink, warpage etc. and reduce the cycle time of injection molding due to rapid crystallization. Application: Injection Molding / automobile applications, industrial parts for electronic, large container Characteristics: High Stiffness, High Impact Strength&&

About

Y UPLENE BX3900 is a high crystalline propylene impact copolymer designed for injection molding applications. YUPLENE BX3900 has excellent properties in stiffness, flow, mechanical properties, heat resistance and impact strength, which make YUPLENE BX3900 suitable for auto parts, electric appliances, large size containers, thin wall and very high speed injection applications. This is not a chemical cracked grade so it is free from surface gas mark. YUPLENE BX3900 can reduce various injection problems such as surface trouble, shrink, warpage etc. and reduce the cycle time of injection molding due to rapid crystallization. Application: Injection Molding / automobile applications, industrial parts for electronic, large container Characteristics: High Stiffness, High Impact Strength&&

Product Description
Supplier	SKC
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Heat Resistance, Good
Availabilitys	North America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Melt Flow Rate	60	g/10min	ASTM D1238
Spiral flow length	＞800	mm	Internal Method

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	155	℃	ASTM D1525
Hot deformation temperature	135	℃	ASTM D648

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	330	kg/cm²	ASTM D638
Tensile strain
fracture	＜100	%	ASTM D638
Bending modulus	19000	kg/cm²	ASTM D790
Rockwell hardness
R-level	105		ASTM D785

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
-20℃	4.0	kg.cm/cm	ASTM D256
23℃	6.5	kg.cm/cm	ASTM D256

Aging performance	Nominal value	Unit	Test method
Accelerate oven aging
150°C	360	hr	ASTM D3012

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.