| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 300℃，1.20 kg | 15 | g/10min | ISO 1133 |
| Water absorption rate | |||
| 23℃，24 hr | 0.3 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，4 mm | 70P | kJ/m² | ISO 180/A |
| Charpy Notched Impact Strength | |||
| 23℃，4 mm | 70P | kJ/m² | ISO 79/1eA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 50 mm/min | 64 | MPa | ISO 527-2/50 |
| Tensile modulus | |||
| 50 mm/min | 2400 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 50 mm/min | 100 | % | ISO 527-2/50 |
| Bending modulus | |||
| 2 mm/min | 2400 | MPa | ISO 178 |
| bending strength | |||
| 2 mm/min | 97 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 146 | ℃ | ISO 11357-2 |
| Hot deformation temperature | |||
| 1.80 MPa | 124 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B120 | 145 | ℃ | ISO 306 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 1 mm | 88 | % | ISO 13468-2 |
| Haze | |||
| 1 mm-2.54 mm | ＜0.8 | % | ISO 14782 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |