| About |
|---|
| Zenite® ZE55201 is a 50% mineral/glass fiber reinforced liquid crystal polymer for injection molding. and It is specifically suitable for applications requiring ultra flatness.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | 液态聚合物 |
| Material Status | Commercial: Active |
| Features | Lubricating,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 15800 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 88.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 1.4 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 12500 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 165 | MPa | ISO 178 |
| compressive strength | |||
| 1% strain | 21.3 | MPa | ISO 604 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.6 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 290 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 300 | ℃ | ISO 75-2/B |
| Melting temperature | 335 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 2.7E-5 | 1/℃ | ISO 11359-2 |
| MD | 1.5E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 37 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 4.00 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 0.031 | IEC 60250 | |
| 1 MHz | 0.031 | IEC 60250 | |
| Compared to the leakage tracing index | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| Extreme oxygen index | 41 | % | ISO 4589-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.85 | g/cm³ | ISO 1183 |
| Density of Melt | 1.620 | g/cm³ | Internal Method |
| Specific Heat Capacity of Melt | 1500 | J/kg/℃ | Internal Method |
| Thermal Conductivity of Melt | 0.40 | W/m/K | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 320 to 330 | °C | |
| Barrel middle temperature | 335 to 345 | °C | |
| Barrel front temperature | 335 to 345 | °C | |
| Nozzle temperature | 335 to 345 | °C | |
| Processing (melt) temperature | 330 to 350 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection pressure | 50.0 to 150 | MPa | |
| Hold pressure | 50.0 to 150 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Ejection temperature | 270 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |