Zenite® ZE55205 is a black reinforced LCP resin with a high dielectric constant.&&

Product Description
Supplier	Celanese
Generic	液态聚合物
Material Status	Commercial: Active
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.89	g/cm³	ISO 1183
Shrinkage rate			ISO 294-4
TD	0.60	%	ISO 294-4
MD	0.10	%	ISO 294-4

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	14300	MPa	ISO 527-2/1A/1
tensile strength
fracture	125	MPa	ISO 527-2/1A/5
Tensile strain
fracture	2.5	%	ISO 527-2/1A/5
Bending modulus
23℃	12200	MPa	ISO 178
bending strength
23℃	190	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	30	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength
23℃	36	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch
23℃	29	kJ/m²	ISO 180-1A
Notched impact strength of cantilever beam
23℃	35	kJ/m²	ISO 180/1U

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	276	℃	ISO 75-2/A

Electrical performance	Nominal value	Test method
Relative permittivity
1 MHz	4.52	IEC 60250
2.05 GHz	6.07	Internal Method
Dissipation factor
1 MHz	0.019	IEC 60250
2.05 GHz	4.0E-3	Internal Method

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	150	°C
Drying time	5.0	hr
Recommended maximum moisture content	0.010	%
Hopper temperature	20 to 30	°C
Barrel rear temperature	320 to 330	°C
Barrel middle temperature	335 to 345	°C
Barrel front temperature	335 to 345	°C
Nozzle temperature	335 to 345	°C
Processing (melt) temperature	330 to 350	°C
Mold temperature	80 to 120	°C
Injection pressure	50.0 to 150	MPa
Hold pressure	50.0 to 150	MPa
Back pressure	0.00 to 3.00	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.