| About |
|---|
| Product Description | |
|---|---|
| Supplier | ZYPEEK |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| 23℃ | 87 | D 级 | ISO 868 |
| compressive strength | |||
| 23℃ | 250 | MPa | ISO 604 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.5 | % | ISO 527 |
| Bending modulus | |||
| 23℃ | 11500 | MPa | ISO 178 |
| bending strength | |||
| Fracture, 23 ℃ | 275 | MPa | ISO 178 |
| tensile strength | |||
| Fracture, 23 ℃ | 185 | MPa | ISO 527 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Water absorption rate | |||
| 23 ℃, 24hr, 3.2mm thick stretching rod | 0.04 | % | ISO 62-1 |
| Equilibrium, 23 ℃ | 0.3 | % | ISO 62-1 |
| Shrinkage rate | |||
| MD | 0.8 | % | ISO 294-4 |
| TD | 0.3 | % | ISO 294-4 |
| Melt Flow Rate | |||
| 380℃，5.0kg | 28 | g/10min | ISO 1133 |
| Density | |||
| crystallization | 1.52 | g/cm³ | ISO 1183 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 9 | kJ/m² | ISO 180/A |
| Notched impact strength of cantilever beam | 50 | kJ/m² | ISO 180/U |
| Charpy Unnotch Impact strength | 50 | kJ/m² | ISO 179/1U |
| Charpy Notched Impact Strength | 7.5 | kJ/m² | ISO 179-1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal conductivity coefficient | ISO 22007-4 | ||
| 23℃ | 0.3 | W/m/K | ISO 22007-4 |
| melting point | 343 | ℃ | ISO 11357 |
| Tg (starting) | 143 | ℃ | ISO 11357 |
| Specific heat capacity | |||
| 23℃ | 1.7 | kJ/kg /℃ | DSC |
| Linear coefficient of thermal expansion | |||
| Below Tg along the flow direction | 20 | ppm/K | ISO 11359 |
| Above Tg along the flow direction | 20 | ppm/K | ISO 11359 |
| Hot deformation temperature | |||
| 1.8 Mpa | 335 | ℃ | ISO 75-f |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dissipation factor | |||
| 23℃，1 MHz | 0.004 | IEC 60250 | |
| Dielectric constant | |||
| 23 ℃, 1 kHz | 3.3 | IEC 60250 | |
| Compared to the leakage tracing index | 150 | V | IEC 60112 |
| Dielectric strength | |||
| 2 mm | 23 | kV/mm | IEC 60243-1 |
| Volume resistivity | |||
| 275 ℃ | – | ohms·cm | IEC 60093 |
| 23 ℃，1V | 10^16 | ohms·cm | IEC 60093 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |