| 15％玻璃纤维增强尼龙6 |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Glass fiber reinforced |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Fracture stress | 133 | MPa | ISO 527-1/2 |
| Fracture strain | 4 | % | ISO 527-1/2 |
| Tensile modulus | 6000 | MPa | ISO 527-1-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 220 | ℃ | ISO 75-1/2 |
| 1.8 MPa | 200 | ℃ | ISO 75-1/2 |
| Linear coefficient of thermal expansion | |||
| MD | 3.8E-5 | /℃ | ASTM E 831 |
| TD | 1.2E-4 | /℃ | ASTM E 831 |
| Melting point temperature | |||
| 10℃/min | 223 | ℃ | ISO 3146C |
| Vicat Softening Temp | |||
| B50 | 214 | ℃ | ISO 306 |
| Flame retardant level | |||
| 1.60 mm | HB | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Humidity absorption | 2.5 | % | ISO 62 |
| Water absorption rate | |||
| Balance, 50% RH | 7.6 | % | ISO 62 |
| Shrinkage rate | |||
| MD | 0.3 | % | ISO 2577 |
| TD | 1.1 | % | ISO 2577 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| -30℃ | 45 | kJ/m² | ISO 179/1eU |
| 23℃ | 45 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| -30℃ | 6 | kJ/m² | ISO 179/1eA |
| 23℃ | 7 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 5 | kJ/m² | ISO 180-1A |
| 23℃ | 6 | kJ/m² | ISO 180-1A |
| Process Conditions | |||
|---|---|---|---|
| Processing conditions | Nominal value | Unit | Test method |
| Melt temperature range | 260-280 | °C | |
| Mold temperature range | 65-120 | °C | |
| Drying time, dehumidifier dryer | 2-4 | h | |
| drying temperature | 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |