| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PA6 |
| Material Status | Commercial: Negative |
| Features | Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 6500 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 130 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.3 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 5.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 40 | kJ/m² | ISO 179/1eU |
| 23℃ | 40 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 204 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 215 | ℃ | ISO 306 |
| Melting temperature | 221 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | ISO 11359-2 | ||
| — | 9.0E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 to 23 ℃ | 7.8E-5 | cm/cm/℃ | ISO 11359-2 |
| 55 to 160 ℃ | 1.0E-4 | cm/cm/℃ | ISO 11359-2 |
| MD | ISO 11359-2 | ||
| — | 1.6E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 to 23 ℃ | 3.5E-5 | cm/cm/℃ | ISO 11359-2 |
| 55 to 160 ℃ | 1.5E-5 | cm/cm/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 22 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Burning rate | |||
| 1 mm | 25 | mm/min | ISO 3795 |
| Flammability level | |||
| 1.5 mm | HB | IEC 60695-11-10, -20 | |
| Extreme oxygen index | 21 | % | ISO 4589-2 |
| FMVSS flame retardant rating | B | FMVSS 302 | |
| Fogging（Gvalue，condensate） | 0.0 | g | ISO 6452 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Emissions of organic compounds | 8.50 | µgC/g | VDA 277 |
| Odor | 4.00 | VDA 270 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.80 | % | ISO 294-4 |
| MD | 0.30 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 7.6 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 2.5 | % | ISO 62 |
| Thermal Conductivity of Melt | 0.20 | W/m/K |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | — | null |
| Drying time – hot air dryer | 2.0 to 4.0 | — | null |
| Recommended maximum moisture content | 0.20 | — | null |
| Processing (melt) temperature | 260 to 280 | — | null |
| Melt Temperature, Optimal | 270 | — | null |
| Mold temperature | 70 to 120 | — | null |
| Mold Temperature, Optimal | 100 | — | null |
| Maintaining pressure | 50.0 to 100 | — | null |
| Drying Recommended | yes | — | null |
| Hold Pressure Time | 3.00 | — | null |
| Maximum Screw Tangential Speed | 200 | — | null |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |