| 20% Glass Reinforced, Heat Stabilized, Polyamide 66 Developed for Blow Molding&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40℃ | 7.5 | kJ/m² | ISO 179/1eA |
| -30℃ | 8.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 40 | kJ/m² | ISO 179/1eU |
| 23℃ | 80 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 8.0 | kJ/m² | ISO 180-1A |
| 23℃ | 14 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 73 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 239 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 257 | ℃ | ISO 75-2/B |
| Glass transition temperature | 60.0 | ℃ | ISO 11357-2 |
| Melting temperature | 260 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| FMVSS flame retardant rating | SE | FMVSS 302 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6500 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 120 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 4.0 | % | ISO 527-2 |
| Tensile Creep Modulus（1 hr） | — | MPa | ISO 899-1 |
| Tensile creep modulus | |||
| 1000 hr | — | MPa | ISO 899-1 |
| Bending modulus | 6000 | MPa | ISO 178 |
| bending strength | 160 | MPa | ISO 178 |
| shear modulus | 1400 | MPa | ISO 6721 |
| Poisson’s ratio | — | ISO 527 | |
| Ball hardness | |||
| H 961/30 | 225 | MPa | ISO 2039-1 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.70 | % | ISO 294-4 |
| MD | 0.50 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 5.2 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 1.6 | % | ISO 62 |
| Viscosity number | |||
| 96% H2SO4 | 155 | cm³/g | ISO 307 |
| Melt density | 1.07 | g/cm³ | |
| Apparent viscosity of melt | |||
| 280℃，1000 sec^-1 | 330000 | mPa·s | ISO 11443 |
| Ejection temperature | 210 | ℃ | |
| Specific Heat Capacity of Melt | 2000 | J/kg/℃ | |
| Thermal Conductivity of Melt | 0.20 | W/m/K |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | — | |
| Drying time – hot air dryer | 2.0 to 4.0 | — | |
| Recommended maximum moisture content | 0.20 | — | |
| Processing (melt) temperature | 285 to 305 | — | |
| Melt Temperature, Optimum | 295 | — | |
| Mold temperature | 50 to 100 | — | |
| Mold Temperature, Optimum | 90 | — | |
| Hold pressure | 50.0 to 100 | — | |
| Drying Recommended | yes | — | |
| Hold Pressure Time | 3.00 | — | |
| Maximum Screw Tangential Speed | 200 | — | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Assessed |
| 3. Derived from Similar Grade |
| 4. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |