| Unreinforced High Viscosity Polyamide 66 Developed for Food Contact Applications&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | High Viscosity,Food contact compliance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 3000 | MPa | |
| tensile strength | |||
| yield | 84.0 | MPa | |
| Tensile strain | |||
| yield | 4.4 | % | |
| Nominal tensile fracture strain | > 50 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 7.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 205 | ℃ | |
| 1.8 MPa, unannealed | 74.0 | ℃ | |
| Melting temperature | 263 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 1.0E-4 | 1/℃ | |
| TD | 1.0E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+13 | ohms·cm | |
| Relative permittivity | |||
| 100 Hz | 3.90 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 1 mm | < 100 | mm/min | |
| FMVSS flame retardant rating | B |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | |
| Shrinkage rate | |||
| MD | 1.6 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 8.5 | % | |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 2.7 | % | |
| Viscosity number | |||
| 96% H2SO4 | 360 | cm³/g | |
| Ejection temperature | 190 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Melt Temperature, Optimum | 290 | °C | |
| Mold temperature | 50 to 90 | °C | |
| Mold Temperature, Optimum | 70 | °C | |
| Hold pressure | 50.0 to 100 | MPa | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Maximum Screw Tangential Speed | 24 | m/min | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 3. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |