| About |
|---|
| 25% Glass Reinforced, Flame Retardant, Polyamide 66/6T&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PA 66/6T |
| Material Status | Commercial: Active |
| Features | Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.1 | % | ISO 294-4 |
| TD | 0.6 | % | ISO 294-4 |
| Water absorption rate | |||
| 2.00 mm | 4.0 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃，50% RH | 90 | MPa | ISO 527-2 |
| 23℃ | 109 | MPa | ISO 527-2 |
| Tensile strain | |||
| 23℃，50%RH | 2.2 | % | ISO 527-2 |
| Fracture, 23 ℃ | 2.2 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃，50% RH | 8700 | MPa | ISO 527-2 |
| 23℃ | 8900 | MPa | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 236 | ℃ | ISO 75-2/Af |
| Melting temperature | 267 | ℃ | ISO 11357-3 |
| Vicat Softening Temp | |||
| Linear coefficient of thermal expansion | |||
| Maximum operating temperature | 160 | ℃ | IEC 60216-1 |
| Maximum operating temperature | 190 | ℃ | IEC 60216-1 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Insulation strength | |||
| 50%RH | 35 | KV/mm | IEC 60243-1 |
| Dissipation factor | |||
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75mm | V-0 | UL 94 | |
| 1.50mm | V-0，5VA | UL 94 | |
| 3.00mm | V-0，5VA | UL 94 | |
| Extreme oxygen index | 32 | % | ISO 4589-2 |
| Igniting temperature of the hot wire | |||
| 0.75 mm | 725 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 725 | ℃ | IEC 60695-2-12 |
| 3 mm | 725 | ℃ | IEC 60695-2-12 |
| Relative temperature of heating wire | |||
| 0.75mm | 960 | ℃ | IEC 60695-2-13 |
| 1.50mm | 960 | ℃ | IEC 60695-2-13 |
| 3.00mm | 960 | ℃ | IEC 60695-2-13 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Spray temperature | 210 | ℃ |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 35 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 4.6 | kJ/m² | ISO 179/1eA |
| -30℃ | 4.5 | kJ/m² | ISO 179/1eA |
| -30℃ | 4.5 | kJ/m² | ISO 179/1eA |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Water content | 0.2 | % | |
| Spray temperature | 210 | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 3. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |