| 35% Glass Reinforced, PPA, High Performance Polyamide Developed for Electrical and Electronics Applications&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | North America,Africa & Middle East ,Latin America,Europe,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Molding shrinkage | |||
| Parallel | 0.2 | % | ISO 294-4 |
| Normal | 0.6 | % | ISO 294-4 |
| Moisture Absorption | 1.4 | % | ISO 62 |
| Water Absorption | 4 | % | ISO 62 |
| Density | 12.3 | lb/gal | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| Dry | 12420 | MPa | ISO 527 |
| Wet Cond | 11040 | MPa | ISO 527 |
| Tensile Stress | |||
| Broken BRK, dry dry | 227.7 | MPa | ISO 527 |
| Broken BRK, wet Cond | 207 | MPa | ISO 527 |
| Tensile Strain | |||
| Broken BRK, dry dry | 2.4 | % | ISO 527 |
| Broken BRK, wet Cond | 2.2 | % | ISO 527 |
| Flexural Modulus | |||
| Dry | 11178 | MPa | ISO 178 |
| Wet Cond | 11592 | MPa | ISO 178 |
| Flexural Strength | |||
| Dry | 297.39 | MPa | ISO 178 |
| Wet Cond | 282.9 | MPa | ISO 178 |
| Poisson’s ratio | |||
| Dry | 0.33 | ||
| Wet Cond | 0.33 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 300 | ℃ | ISO 11357-3 |
| Hot deformation temperature HDT | |||
| 1.8 MPa | 265 | ℃ | ISO 75-1/-2 |
| Coeff. of linear thermal expansion | |||
| Parallel, -40-23 ℃ | 0.1 | E-4/°F | ISO 11359-2 |
| Parallel | 0.1 | E-4/°F | ISO 11359-2 |
| Parallel, 55-160 ℃ | 0.0722 | E-4/°F | ISO 11359-2 |
| Normal, -40-23 ℃ | 0.278 | E-4/°F | ISO 11359-2 |
| Normal | 0.306 | E-4/°F | ISO 11359-2 |
| Normal, 55-160 ℃ | 0.444 | E-4/°F | ISO 11359-2 |
| Specification of Heat Capacity of Melt | 0.684 | BTU/(lb·F) | |
| Specification: Solid Heat Capacity | 0.229 | BTU/(lb·F) |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Oxygen Index | 23 | % | ISO 4589-2 |
| Glow Wire Flammability Index (GWFI) | |||
| 1 mm | 749 | ℃ | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (GWIT) | |||
| 1 mm | 749 | ℃ | IEC 60695-2-13 |
| 3 mm | 798 | ℃ | IEC 60695-2-13 |
| FMVSS flame retardant rating | B | FMVSS 302 | |
| Burning Speed | <80 | in/min | FMVSS 302 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 100Hz | 4.4 | IEC 62631-2-1 | |
| 1MHz | 4.3 | IEC 62631-2-1 | |
| Dissipation Factor | |||
| 100Hz | 160 | E-4 | IEC 62631-2-1 |
| 1MHz | 190 | E-4 | IEC 62631-2-1 |
| Volume Resistance | |||
| Dry | >1E13 | ohm·m | IEC 62631-3-1 |
| Wet Cond | >1E13 | ohm·m | IEC 62631-3-1 |
| Electric strength | |||
| Dry | 813 | kV/in | IEC 60243-1 |
| Wet Cond | 787 | kV/in | IEC 60243-1 |
| Compared Tracking Index | 525 | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 | ℃ | |
| Drying Time | 6-8 | hr | |
| Maximum Moisture Content | 0.10 | % | |
| Melt Temperature | 320-330 | ℃ | |
| Mold Temperature | 140-180 | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. First Heat |
| 3. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |