| About |
|---|
| 35% Glass Reinforced, PPA, High Performance Polyamide&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | North America,Latin America,Europe,Africa & Middle East ,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | |||
| 325℃，4.76lb | 19 | cm³/10min | ISO 1133 |
| Melt Flow Rate | |||
| 325℃，4.76lb | 21 | g/10min | ISO 1133 |
| Molding shrinkage | |||
| Parallel | 0.2 | % | ISO 294-4 |
| Normal | 0.6 | % | ISO 294-4 |
| Moisture Absorption | 1.4 | % | ISO 62 |
| Water Absorption | 4 | % | ISO 62 |
| Density | 12.3 | lb/gal | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| Dry | 11730 | MPa | ISO 527 |
| Wet Cond | 11730 | MPa | ISO 527 |
| Tensile Stress | |||
| Broken BRK, dry dry | 200.1 | MPa | ISO 527 |
| Broken BRK, wet Cond | 193.2 | MPa | ISO 527 |
| Tensile Strain | |||
| Broken BRK, dry dry | 2.3 | % | ISO 527 |
| Broken BRK, wet Cond | 2 | % | ISO 527 |
| Flexural Modulus | |||
| Dry | 10488 | MPa | ISO 178 |
| Ball indentation hardness | 210.5 | MPa | ISO 2039-1 |
| Poisson’s ratio | |||
| Dry | 0.33 | ||
| Wet Cond | 0.33 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| Dry | 50.4 | kJ/m² | ISO 179/1eU |
| Wet Cond | 39.9 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| Dry | 9.03 | kJ/m² | ISO 179/1eA |
| Wet Cond | 7.98 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 300 | ℃ | ISO 11357-3 |
| Glass Transition Temperature | |||
| Dry | 135 | ℃ | ISO 11357-2 |
| Wet Cond | 95 | ℃ | ISO 11357-2 |
| Hot deformation temperature HDT | |||
| 1.8 MPa | 260 | ℃ | ISO 75-1/-2 |
| 0.45 MPa | 277 | ℃ | ISO 75-1/-2 |
| Coeff. of linear thermal expansion | |||
| Parallel, -40-23 ℃ | 0.111 | E-4/°F | ISO 11359-2 |
| Parallel | 0.11 | E-4/°F | ISO 11359-2 |
| Normal, -40-23 ℃ | 0.306 | E-4/°F | ISO 11359-2 |
| Normal | 0.322 | E-4/°F | ISO 11359-2 |
| Specification of Heat Capacity of Melt | 0.684 | BTU/(lb·F) | |
| Specification: Solid Heat Capacity | 0.229 | BTU/(lb·F) |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| FMVSS flame retardant rating | B | FMVSS 302 | |
| Burning Speed | 1.1 | in/min | FMVSS 302 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1E13 | ohm·m | IEC 62631-3-1 |
| Electric strength | |||
| Dry | 864 | kV/in | IEC 60243-1 |
| Wet Cond | 838 | kV/in | IEC 60243-1 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 | ℃ | |
| Drying Time | 6.0 to 8.0 | hr | |
| Maximum Moisture Content | 0.10 | % | |
| Melt Temperature | 320 to 330 | ℃ | |
| Melt Temperature, Optimal | 325 | ℃ | |
| Mold Temperature | 140 to 180 | ℃ | |
| Mold Temperature, Optimal | 150 | ℃ | |
| Drying Recommended | yes | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. First Heat |
| 3. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |