| 35% Glass Reinforced, PPA, High Performance Polyamide with Improved Surface Appearance&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Heat Stabilized,Good surface appearance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Molding shrinkage | |||
| Parallel | 0.2 | % | ISO 294-4 |
| Normal | 0.5 | % | ISO 294-4 |
| Moisture Absorption | 1.4 | % | ISO 62 |
| Density | 12.2 | lb/gal | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| Dry | 11730 | MPa | ISO 527 |
| Tensile Stress | |||
| Broken BRK, dry dry | 213.1 | MPa | ISO 527 |
| Tensile Strain | |||
| Broken BRK, dry dry | 2.6 | % | ISO 527 |
| Flexural Modulus | |||
| Dry | 10281 | MPa | ISO 178 |
| Poisson’s ratio | |||
| Dry | 0.33 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 10.92 | kJ/m² | ISO 179/1eA |
| -30℃ | 10.08 | kJ/m² | ISO 179/1eA |
| -40℃ | 10.08 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact strength | |||
| -40℃ | 9.996 | KJ/m² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 300 | ℃ | ISO 11357-3 |
| Glass Transition Temperature | |||
| Dry | 135 | ℃ | ISO 11357-2 |
| Wet Cond | 95 | ℃ | ISO 11357-2 |
| Hot deformation temperature HDT | |||
| 1.8 MPa | 266 | ℃ | ISO 75-1/-2 |
| Coeff. of linear thermal expansion | |||
| Parallel, -40-23 ℃ | 0.0722 | E-4/°F | ISO 11359-2 |
| Parallel | 0.10 | E-4/°F | ISO 11359-2 |
| Parallel, 55-160 ℃ | 0.0944 | E-4/°F | ISO 11359-2 |
| Normal, -40-23 ℃ | 0.2 | E-4/°F | ISO 11359-2 |
| Normal | 0.278 | E-4/°F | ISO 11359-2 |
| Normal, 55-160 ℃ | 0.367 | E-4/°F | ISO 11359-2 |
| Specification of Heat Capacity of Melt | 0.684 | BTU/(lb·F) | |
| Specification: Solid Heat Capacity | 0.229 | BTU/(lb·F) |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| FMVSS flame retardant rating | B | FMVSS 302 | |
| Burning Speed | 0.906 | in/min | FMVSS 302 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1E13 | ohm·m | IEC 62631-3-1 |
| Electric strength | |||
| Dry | 864 | kV/in | IEC 60243-1 |
| Compared Tracking Index | 600 | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 | °C | |
| Drying Time | 6.0 to 8.0 | hr | |
| Maximum Moisture Content | 0.10 | % | |
| Melt Temperature | 320 to 330 | °C | |
| Melt Temperature, Optimal | 325 | °C | |
| Mold Temperature | 140 to 180 | °C | |
| Mold Temperature, Optimal | 150 | °C | |
| Drying Recommended | yes | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |