| About |
|---|
| 50% Glass Reinforced High Performance Polyamide with Improved Impact and Stiffness&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | High impact resistance,Heat Stabilized,Good Rigidity,HB |
| Availabilitys | Latin America,Europe,North America,Asia Pacific,Africa & Middle East |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Molding shrinkage | |||
| Parallel | 0.2 | % | ISO 294-4 |
| Normal | 0.4 | % | ISO 294-4 |
| Density | 13.3 | lb/gal | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| Dry | 16560 | MPa | ISO 527 |
| Wet Cond | 16560 | MPa | ISO 527 |
| Tensile Stress | |||
| Broken BRK, dry dry | 248.4 | MPa | ISO 527 |
| Broken BRK, wet Cond | 213.9 | MPa | ISO 527 |
| Tensile Strain | |||
| Broken BRK, dry dry | 2.8 | % | ISO 527 |
| Broken BRK, wet Cond | 3.2 | % | ISO 527 |
| Flexural Modulus | 15042 | MPa | ISO 178 |
| Poisson’s ratio | |||
| Dry | 0.33 | ||
| Wet Cond | 0.33 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 94.5 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 14.91 | kJ/m² | ISO 179/1eA |
| -40℃ | 14.07 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact strength | |||
| 23℃ | 15 | KJ/m² | ISO 180/1A |
| -40℃ | 13.5 | KJ/m² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 260 | ℃ | ISO 11357-3 |
| Glass Transition Temperature | |||
| Dry | 85 | ℃ | ISO 11357-2 |
| Wet Cond | 45 | ℃ | ISO 11357-2 |
| Hot deformation temperature HDT | |||
| 1.80 MPa | 238 | ℃ | ISO 75-1/-2 |
| Coeff. of linear thermal expansion | |||
| Parallel, -40-23 ° C | 0.0944 | E-4/°F | ISO 11359-2 |
| Parallel | 0.08 | E-4/°F | ISO 11359-2 |
| Parallel, 55-160 ° C | 0.0556 | E-4/°F | ISO 11359-2 |
| Normal, -40-23 ° C | 0.306 | E-4/°F | ISO 11359-2 |
| Normal | 0.306 | E-4/°F | ISO 11359-2 |
| Normal, 55-160 ° C | 0.611 | E-4/°F | ISO 11359-2 |
| Relative Temperature Index (RTI) | |||
| Electrical | |||
| 0.75 mm | 65 | ℃ | UL-746B |
| 1.5 mm | 65 | ℃ | UL-746B |
| 3.0 mm | 65 | ℃ | UL-746B |
| Impact | |||
| 0.75 mm | 65 | ℃ | UL-746B |
| 1.5 mm | 65 | ℃ | UL-746B |
| 3.0 mm | 65 | ℃ | UL-746B |
| Strength | |||
| 0.75 mm | 65 | ℃ | UL-746B |
| 1.5 mm | 65 | ℃ | UL-746B |
| 3.0 mm | 65 | ℃ | UL-746B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.6 mm | HB | UL 94 | |
| 0.8 mm | HB | UL 94 | |
| Oxygen Index | 27 | % | ISO 4589-2 |
| FMVSS flame retardant rating | B | ISO 3795 | |
| Burning Speed | 0.984 | in/min | ISO 3795 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1E13 | ohm·m | IEC 62631-3-1 |
| Compared Tracking Index | 600 | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 | ℃ | |
| Drying Time | 6.0 to 8.0 | hr | |
| Maximum Moisture Content | 0.10 | % | |
| Melt Temperature | 280 to 300 | ℃ | |
| Melt Temperature, Optimal | 290 | ℃ | |
| Mold Temperature | 90 to 110 | ℃ | |
| Drying Recommended | yes | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. First Heat |
| 3. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |