| 50% Glass Reinforced High Performance Polyamide with Low Warpage and High Stiffness&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.58 | g/cm³ | |
| Shrinkage rate | |||
| TD | 0.30 | % | |
| MD | 0.10 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 17000 | MPa | |
| tensile strength | |||
| fracture | 270 | MPa | |
| Tensile strain | |||
| fracture | 2.4 | % | |
| Tensile creep modulus | |||
| 1 hr | — | MPa | |
| 1000 hr | — | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 14 | kJ/m² | |
| 23℃ | 15 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 90 | kJ/m² | |
| 23℃ | 90 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 255 | ℃ | |
| 1.8 MPa, unannealed | 250 | ℃ | |
| Melting temperature | 260 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 1.9E-5 | 1/℃ | |
| TD | 5.9E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | |
| Volume resistivity | > 1.0E+15 | ohms·cm | |
| Compared to the leakage tracing index | 550 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | HB | ||
| Burning rate | |||
| 1 mm | < 100 | mm/min | |
| FMVSS flame retardant rating | B |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time – hot air dryer | 6.0 to 8.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Melt Temperature, Optimum | 290 | °C | |
| Mold temperature | 90 to 110 | °C | |
| Drying Recommended | yes | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. First Heat |
| 3. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |