| Zytel® HTN 92G35DH2 BK083是一种HIGH PERFORMANCE POLYAMIDE RESIN产品,含有的填充物为35% 玻璃纤维增强材料。 它可以通过注射成型进行加工,在亚太地区、北美洲、拉丁美洲、欧洲或非洲和中东有供货。 特性包括: 热稳定剂 脱模剂&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PPA |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.90 | % | ISO 294-4 |
| MD | 0.20 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 200 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.4 | % | ISO 527-2 |
| Tensile creep modulus | ISO 899-1 | ||
| 1 hr | — | MPa | ISO 899-1 |
| 1000 hr | — | MPa | ISO 899-1 |
| Bending modulus | 10000 | MPa | ISO 178 |
| bending strength | 272 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 50 | kJ/m² | ISO 179/1eU |
| 23℃ | 55 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 283 | ℃ | ISO 75-2/A |
| Melting temperature | 310 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD | 1.9E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~23℃ | 1.9E-5 | 1/℃ | ISO 11359-2 |
| TD | 6.3E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~23℃ | 6.3E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 32 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |