| 30% Glass Reinforced, Flame Retardant, Non-Halogenated, PPA, High Performance Polyamide with Improved Reflow Soldering Performance&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.90 | % | |
| MD | 0.40 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11700 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 134 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.7 | % | ISO 527-2 |
| Bending modulus | 11300 | MPa | ISO 178 |
| bending strength | 210 | MPa | ISO 178 |
| Poisson’s ratio | 0.33 | ISO 527 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 7.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 35 | kJ/m² | |
| 23℃ | 35 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 314 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 2.0E-5 | 1/℃ | |
| MD：-40~23℃ | 1.7E-5 | 1/℃ | |
| MD：55~160℃ | 2.0E-5 | 1/℃ | |
| TD | 5.1E-5 | 1/℃ | |
| TD：-40~23℃ | 4.3E-5 | 1/℃ | |
| TD：55~160℃ | 8.4E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Dielectric strength | 33 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 0.40 mm | 960 | ℃ | |
| 1.5 mm | 960 | ℃ | |
| 3.0 mm | 960 | ℃ | |
| Igniting temperature of the hot wire | |||
| 0.4 mm | 750 | ℃ | |
| 1.5 mm | 800 | ℃ | |
| 3 mm | 825 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time – hot air dryer | 6.0 to 8.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Processing (melt) temperature | 325 to 335 | °C | |
| Mold temperature | 110 to 130 | °C | |
| Drying Recommended | yes | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. First Heat |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |