| 45% Glass Reinforced, Flame Retardant, PPA, High Performance Polyamide&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | V-0,Flame Characteristics |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe,Latin America,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.76 | g/cm³ | ISO 1183 |
| Molding shrinkage | ISO 294-4 | ||
| TD | 0.60 | % | ISO 294-4 |
| MD | 0.20 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 17000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Broken BRK | 175 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK | 1.3 | % | ISO 527-2 |
| Flexural Modulus | 15200 | MPa | ISO 178 |
| Flexural Strength | 290 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40℃ | 13 | kJ/m² | ISO 179/1eA |
| 23℃ | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 40 | kJ/m² | ISO 179/1eU |
| 23℃ | 42 | kJ/m² | ISO 179/1eU |
| Izod Notched Impact strength | |||
| 23℃ | 12 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 284 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 300 | ℃ | ISO 75-2/B |
| Melting temperature | 310 | ℃ | ISO 11357-3 |
| Coeff. of linear thermal expansion | |||
| TD | ISO 11359-2 | ||
| — | 5.0E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 to 23 ℃ | 5.0E-5 | cm/cm/℃ | ISO 11359-2 |
| 55 to 160 ℃ | 7.5E-5 | cm/cm/℃ | ISO 11359-2 |
| MD | ISO 11359-2 | ||
| — | 1.5E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 to 23 ℃ | 1.5E-5 | cm/cm/℃ | ISO 11359-2 |
| 55 to 160 ℃ | 8.0E-6 | cm/cm/℃ | ISO 11359-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 31 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.90 | IEC 60250 | |
| 1 MHz | 3.60 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 4.5E-3 | IEC 60250 | |
| 1 MHz | 0.011 | IEC 60250 | |
| Compared Tracking Index | 500 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning Speed | |||
| 1 mm | < 100 | mm/min | ISO 3795 |
| Flame Class Rating | UL 94 | ||
| 0.75 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| Flame Class Rating | IEC 60695-11-10, -20 | ||
| 0.75 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | IEC 60695-11-10, -20 | |
| Oxygen Index | 49 | % | ISO 4589-2 |
| FMVSS flame retardant rating | B | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 | ℃ | |
| Drying Time | 6.0 to 8.0 | hr | |
| Maximum Moisture Content | 0.10 | % | |
| Melt Temperature | 320 to 330 | ℃ | |
| Melt Temperature, Optimal | 325 | ℃ | |
| Mold Temperature | 90 to 110 | ℃ | |
| Drying Recommended | yes | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. First Heat |
| 3. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |