| 45% Glass Reinforced, Flame Retardant, Non-Halogenated, PPA, High Performance Polyamide&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics |
| Availabilitys | North America,Latin America,Asia Pacific,Africa & Middle East ,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.60 | g/cm³ | ISO 1183 |
| Molding shrinkage | |||
| TD | 0.50 | % | |
| MD | 0.20 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 15500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Broken BRK | 167 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK | 1.7 | % | ISO 527-2 |
| Flexural Modulus | 15100 | MPa | ISO 178 |
| Flexural Strength | 249 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 8.0 | kJ/m² | |
| 23℃ | 8.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 45 | kJ/m² | |
| 23℃ | 48 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 284 | ℃ | ISO 75-2/A |
| Melting temperature | 310 | ℃ | ISO 11357-3 |
| Coeff. of linear thermal expansion | |||
| MD | 1.5E-5 | 1/℃ | |
| MD：-40~23℃ | 1.3E-5 | 1/℃ | |
| MD：55~160℃ | 1.4E-5 | 1/℃ | |
| TD | 5.0E-5 | 1/℃ | |
| TD：-40~23℃ | 4.3E-5 | 1/℃ | |
| TD：55~160℃ | 8.0E-5 | 1/℃ | |
| Relative Temperature Index (RTI) | |||
| Electrical performance | |||
| 0.40 mm | 140 | ℃ | |
| 0.75 mm | 140 | ℃ | |
| 1.5 mm | 140 | ℃ | |
| 3.0 mm | 140 | ℃ |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 40 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 100 Hz | 4.70 | ||
| 1 MHz | 4.40 | ||
| Dissipation Factor | |||
| 100 Hz | 6.0E-3 | ||
| 1 MHz | 0.012 | ||
| Compared Tracking Index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index GWFI | |||
| 0.40 mm | 960 | ℃ | |
| 0.75 mm | 960 | ℃ | |
| 1.5 mm | 960 | ℃ | |
| 3.0 mm | 960 | ℃ | |
| Glow Wire Ignitability Temperature (GWIT) | |||
| 0.4 mm | 700 | ℃ | |
| 0.75 mm | 750 | ℃ | |
| 1.5 mm | 750 | ℃ | |
| 3 mm | 800 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 | °C | |
| Drying Time | 6.0 to 8.0 | hr | |
| Maximum Moisture Content | 0.10 | % | |
| Melt Temperature | 320 to 325 | °C | |
| Mold Temperature | 90 to 130 | °C | |
| Drying Recommended | yes | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. First Heat |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |