| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Flame Characteristics,V-0,Low warping,Halogen free |
| Availabilitys | Asia Pacific,Europe,Latin America,Africa & Middle East ,North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding shrinkage | ISO 294-4 | ||
| TD | 0.20 | % | ISO 294-4 |
| MD | 0.10 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 17500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Broken BRK | 195 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK | 1.6 | % | ISO 527-2 |
| Flexural Modulus | 16600 | MPa | ISO 178 |
| Flexural Strength | 306 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 50 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 215 | ℃ | ISO 75-2/A |
| Melting temperature | 298 | ℃ | ISO 11357-3 |
| Coeff. of linear thermal expansion | |||
| TD | ISO 11359-2 | ||
| — | 3.8E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 to 23 ℃ | 3.6E-5 | cm/cm/℃ | ISO 11359-2 |
| MD | ISO 11359-2 | ||
| — | 1.2E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 to 23 ℃ | 1.4E-5 | cm/cm/℃ | ISO 11359-2 |
| 55 to 160 ℃ | 1.1E-5 | cm/cm/℃ | ISO 11359-2 |
| Relative Temperature Index (RTI) | |||
| Electrical performance | UL 746 | ||
| 0.40 mm | 65.0 | ℃ | UL 746 |
| 0.75 mm | 65.0 | ℃ | UL 746 |
| 1.5 mm | 65.0 | ℃ | UL 746 |
| 3.0 mm | 65.0 | ℃ | UL 746 |
| Strength mechanical performance | UL 746 | ||
| 0.40 mm | 65.0 | ℃ | UL 746 |
| 0.75 mm | 65.0 | ℃ | UL 746 |
| 1.5 mm | 65.0 | ℃ | UL 746 |
| 3.0 mm | 65.0 | ℃ | UL 746 |
| Impact mechanical performance | UL 746 | ||
| 0.40 mm | 65.0 | ℃ | UL 746 |
| 0.75 mm | 65.0 | ℃ | UL 746 |
| 1.5 mm | 65.0 | ℃ | UL 746 |
| 3.0 mm | 65.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning Speed | |||
| 1 mm | < 100 | mm/min | ISO 3795 |
| Flame Class Rating | UL 94 | ||
| 0.75 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| Flammability level | IEC 60695-11-10, -20 | ||
| 0.75 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | IEC 60695-11-10, -20 | |
| FMVSS flame retardant rating | B | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 | °C | |
| Drying Time | 6.0 to 8.0 | hr | |
| Maximum Moisture Content | 0.10 | % | |
| Melt Temperature | 300 to 315 | °C | |
| Mold Temperature | 70 to 130 | °C | |
| Drying Recommended | yes | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |