| About |
|---|
| 30% Glass Reinforced, Flame Retardant, Non-Halogenated, PPA, High Performance Polyamide Developed for Laser Welding&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics |
| Availabilitys | Asia Pacific,Latin America,Europe,Africa & Middle East ,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | |
| Molding shrinkage | |||
| TD | 0.80 | % | |
| MD | 0.30 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 10800 | MPa | |
| Tensile Strength | |||
| Broken BRK | 148 | MPa | |
| Tensile Strain | |||
| Broken BRK | 2.2 | % | |
| Flexural Modulus | 10500 | MPa | |
| Flexural Strength | 215 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 40 | kJ/m² | |
| 23℃ | 46 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 283 | ℃ | |
| Melting temperature | 310 | ℃ | |
| Coeff. of linear thermal expansion | |||
| MD | 2.5E-5 | 1/℃ | |
| MD：-40~23℃ | 2.1E-5 | 1/℃ | |
| MD：55~160℃ | 2.7E-5 | 1/℃ | |
| TD | 6.8E-5 | 1/℃ | |
| TD：-40~23℃ | 5.7E-5 | 1/℃ | |
| TD：55~160℃ | 1.2E-4 | 1/℃ |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared Tracking Index | 600 | V |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 | °C | |
| Drying Time | 6.0 to 8.0 | hr | |
| Maximum Moisture Content | 0.10 | % | |
| Melt Temperature | 320 to 325 | °C | |
| Mold Temperature | 90 to 130 | °C | |
| Drying Recommended | yes | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. First Heat |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |