| About |
|---|
| 50% Glass Reinforced, Heat Stabilized, Polyamide&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PA Not specified |
| Material Status | Commercial: Active |
| Features | Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.59 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 13.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.60 | % | ISO 294-4 |
| MD | 0.30 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 4.5 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 1.3 | % | ISO 62 |
| Viscosity number | |||
| 96% H2SO4 | 125 | cm³/g | ISO 307 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 17000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 250 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.6 | % | ISO 527-2 |
| Tensile Creep Modulus（1 hr） | — | MPa | ISO 899-1 |
| Tensile creep modulus | |||
| 1000 hr | — | MPa | ISO 899-1 |
| Bending modulus | 16000 | MPa | ISO 178 |
| bending strength | 370 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 16 | kJ/m² | ISO 179/1eA |
| 23℃ | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 80 | kJ/m² | ISO 179/1eU |
| 23℃ | 90 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 254 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 263 | ℃ | ISO 75-2/B |
| Melting temperature | 265 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | ISO 11359-2 | ||
| MD | ISO 11359-2 | ||
| — | 1.4E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 to 23 ℃ | 1.5E-5 | cm/cm/℃ | ISO 11359-2 |
| 55 to 160 ℃ | 5.0E-6 | cm/cm/℃ | ISO 11359-2 |
| — | 6.7E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 to 23 ℃ | 5.6E-5 | cm/cm/℃ | ISO 11359-2 |
| 55 to 160 ℃ | 1.2E-4 | cm/cm/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 1 mm | < 100 | mm/min | ISO 3795 |
| Flammability level | |||
| 1.5 mm | HB | IEC 60695-11-10, -20 | |
| FMVSS flame retardant rating | B | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | — | |
| Drying time – hot air dryer | 2.0 to 4.0 | — | |
| Recommended maximum moisture content | 0.20 | — | |
| Processing (melt) temperature | 285 to 305 | — | |
| Melt Temperature, Optimum | 295 | — | |
| Mold temperature | 70 to 120 | — | |
| Mold Temperature, Optimum | 100 | — | |
| Hold pressure | 50.0 to 100 | — | |
| Drying Recommended | yes | — | |
| Hold Pressure Time | 3.00 | — | |
| Maximum Screw Tangential Speed | 200 | — | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |