| About |
|---|
| Unreinforced, Renewably Sourced, Polyamide 1010 Developed for Extrusion&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PA 1010 |
| Material Status | Commercial: Active |
| Features | Renewable resources |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 1800 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 52.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 4.5 | % | ISO 527-2 |
| Nominal tensile fracture strain | > 50 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 8.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 6.0 | kJ/m² | ISO 180-1A |
| 23℃ | 4.5 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 50.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 120 | ℃ | ISO 75-2/B |
| Glass transition temperature | 50.0 | ℃ | ISO 11357-2 |
| Melting temperature | 202 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 1 mm | < 100 | mm/min | ISO 3795 |
| FMVSS flame retardant rating | B | FMVSS 302 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.0 | % | ISO 294-4 |
| MD | 1.4 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 1.1 | % | ISO 62 |
| Viscosity number | |||
| 96% H2SO4 | 110 | cm³/g | ISO 307 |
| Apparent viscosity of melt | |||
| 250℃，1000 sec^-1 | 230000 | mPa·s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 75 to 80 | — | |
| Drying time | 3.0 to 4.0 | — | |
| Recommended maximum moisture content | 0.060 | — | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |