| About |
|---|
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Bending modulus | 3660 | MPa | ASTM D790 |
| 3600 | MPa | ISO 178 | |
| Tensile modulus | 4200 | MPa | ISO 527-1-2 |
| Tensile strain | |||
| fracture | 9 | % | ISO 527-1/2 |
| fracture | 6 | % | ASTM D638 |
| tensile strength | 90 | MPa | ASTM D638 |
| Fracture elongation | 6 | % | ASTM D638 |
| Tensile strain | |||
| fracture | 9 | % | ISO 527-1/2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -40℃ | 4 | kJ/m² | ISO 179/1eA |
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -40℃ | 7 | kJ/m² | ISO 180-1A |
| 23℃ | 13 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 250 | ℃ | ASTM D648 |
| 1.8 MPa | 220 | ℃ | ASTM D648 |
| deformation temperature | |||
| 0.45MPa | 246 | °C | ISA 75-1/-2 |
| 1.8MPa | 195 | °C | ISA 75-1/-2 |
| Linear expansion coefficient (equilibrium) | |||
| -40~23 | 0.52 | E-4/C | ASTM E831 |
| 23~55 | 0.50 | E-4/C | ASTM E831 |
| 55~160 | 0.46 | E-4/C | ASTM E831 |
| Linear expansion coefficient (normal) | |||
| -40~23 | 0.96 | E-4/C | ASTM E831 |
| 23~55 | 1.18 | E-4/C | ASTM E831 |
| 55~160 | 1.23 | E-4/C | ASTM E831 |
| melting point | 262 | °C | ASTM D3418 |
| Melting temperature | 263 | ℃ | ISO 3146C |
| other | Nominal value | Unit | Test method |
|---|
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Process Conditions | |||
|---|---|---|---|
| Processing conditions | Nominal value | Unit | Test method |
| Melting range | 290-305 | °C | |
| Mold temperature | 65-120 | °C | |
| Processing moisture content | <0.20 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |