Ultramid® T 4381 LDS BK23215

About
Glass fibre and mineral reinforced partially aromatic polyamide for injection moulding. Good toughness, stiffness and strength, low water absorption, high melting point (295 °C). The product is especially tailored for laser direct structuring (LDS). The structured areas can be metallized selectively. The compound is intended specifically for the use in the process of manufacturing conducting path designs according to the German application of the patent 101 32 092 of LPKF Laser & Electronics AG (Osteriede 7 – 30827 Garbsen – Germany). The use of this process asserts a claim for compensation. After purchasing a LPKF laser system the claim is satisfied. Please contact directly LPKF Laser & Electronics AG (http://www.LPKF.de).&&

About

Glass fibre and mineral reinforced partially aromatic polyamide for injection moulding. Good toughness, stiffness and strength, low water absorption, high melting point (295 °C). The product is especially tailored for laser direct structuring (LDS). The structured areas can be metallized selectively. The compound is intended specifically for the use in the process of manufacturing conducting path designs according to the German application of the patent 101 32 092 of LPKF Laser & Electronics AG (Osteriede 7 – 30827 Garbsen – Germany). The use of this process asserts a claim for compensation. After purchasing a LPKF laser system the claim is satisfied. Please contact directly LPKF Laser & Electronics AG (http://www.LPKF.de).&&

Product Description
Supplier	BASF
Generic	PA 6/6T
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Low or no water absorption,Aromatic,Copolymer
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	110	°C
Drying time	8.0	hr
Recommended maximum moisture content	0.15	%
Hopper temperature	80	°C
Barrel rear temperature	300	°C
Barrel middle temperature	310	°C
Barrel front temperature	315	°C
Nozzle temperature	315	°C
Processing (melt) temperature	310 to 330	°C
Mold temperature	70 to 100	°C
Screw Speed	< 300	mm/sec

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.