| Glass fibre and mineral reinforced partially aromatic polyamide for injection moulding. Good toughness, stiffness and strength, low water absorption, high melting point (295 °C). The product is especially tailored for laser direct structuring (LDS). The structured areas can be metallized selectively. The compound is intended specifically for the use in the process of manufacturing conducting path designs according to the German application of the patent 101 32 092 of LPKF Laser & Electronics AG (Osteriede 7 – 30827 Garbsen – Germany). The use of this process asserts a claim for compensation. After purchasing a LPKF laser system the claim is satisfied. Please contact directly LPKF Laser & Electronics AG (http://www.LPKF.de).&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA 6/6T |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Low or no water absorption,Aromatic,Copolymer |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.57 | g/cm³ | ISO 1183 |
| viscosity | |||
| (0.5%，96% H2SO4 | 130 | cm³/g | ISO 307 |
| Water absorption rate | |||
| 23 ℃, saturated | 4.6-5.2 | % | ISO 62 |
| 23℃，50%RH | 0.8-1.2 | % | ISO 62 |
| Shrinkage rate | |||
| MD | 0.6 | % | ISO 2577 |
| TD | 0.8 | % | ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9000 | MPa | ISO 527-1/-2 |
| tensile strength | |||
| fracture | 110 | MPa | ISO 527-1/-2 |
| Tensile strain | 2 | % | ISO 527-1/-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 35 | kJ/m² | ISO 179/1eU |
| -30℃ | 35 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 265 | ℃ | ISO 75-1/-2 |
| Linear coefficient of thermal expansion | |||
| M：23-80℃ | 30 | E-6/K | ISO 11359-1/-2 |
| TD：23-80℃ | 50 | E-6/K | ISO 11359-1/-2 |
| Melting temperature | |||
| DSC | 295 | ℃ | ISO 11357-1/-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 1MHz | 4.2 | IEC 60250 | |
| Loss factor | |||
| 1MHz | 150 | E-4 | IEC 60250 |
| Volume resistivity | >1E+13 | Ohm*m | IEC 60093 |
| Leakage Traceability Index, CTI, Test Fluid A | 600 | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.6 mm | HB | IEC 60695-11-10 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 310-330 | °C | |
| Mold temperature | 70-100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |