| About |
|---|
| Partially aromatic polyamide for injection molding and extrusion. High toughness, stiffness and strength, low water absorption, high melting point (295°C).&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA 6/6T |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Low or no water absorption,Aromatic,Copolymer |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data |
|---|
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time | 8.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Hopper temperature | 80 | °C | |
| Barrel rear temperature | 300 | °C | |
| Barrel middle temperature | 310 | °C | |
| Barrel front temperature | 315 | °C | |
| Nozzle temperature | 315 | °C | |
| Processing (melt) temperature | 310 to 330 | °C | |
| Mold temperature | 70 to 100 | °C | |
| Residence Time | < 5.0 | min | |
| Screw Speed | < 300 | mm/sec | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 320°C (unreinforced) or 330°C (reinforced), TW = 80°C |
| 3. strain <= 0.5%, 23°C |
| 4. 5000 h |
| 5. 20000 h |
| 6. 60*60*1 mm³ |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |